Is an oxygen inhibition layer essential for the interfacial bonding between resin composite layers?

Sun-Young Kim; Byeong-Hoon Cho; Seung-Ho Baek; In-Bog Lee

doi:10.5395/JKACD.2008.33.4.405

Journal List > J Korean Acad Conserv Dent > v.33(4) > 1056318

Go to TopGo to Top Go to BottomGo to Bottom

TOOLS

Kim, Cho, Baek, and Lee: Is an oxygen inhibition layer essential for the interfacial bonding between resin composite layers?

Original Article

Journal of Korean Academy of Conservative Dentistry

Journal of Korean Academy of Conservative Dentistry 2008; 33(4): 405-412.

Published online: 31 July 2008

DOI: https://doi.org/10.5395/JKACD.2008.33.4.405

Is an oxygen inhibition layer essential for the interfacial bonding between resin composite layers?

Sun-Young Kim, Byeong-Hoon Cho, Seung-Ho Baek, In-Bog Lee

Department of Conservative Dentistry, School of Dentistry, Seoul National University, Korea.

Corresponding Author: In-Bog Lee. Department of Conservative Dentistry, School of Dentistry, Seoul National University, 275-1 Yeongeon-Dong, Jongno-Gu, Seoul, 110-768, Korea. Tel: 82-2-2072-3953, Fax: 82-2-2072-3859, inboglee@snu.ac.kr

Received 4 June 2008 Revised 4 July 2008 Accepted 8 July 2008

(open-access):

This is an Open Access article distributed under the terms of the Creative Commons Attribution Non-Commercial License (http://creativecommons.org/licenses/by-nc/3.0/) which permits unrestricted non-commercial use, distribution, and reproduction in any medium, provided the original work is properly cited.

Abstract

This study was aimed to investigate whether an oxygen inhibition layer (OIL) is essential for the interfacial bonding between resin composite layers or not.

A composite (Z-250, 3M ESPE) was filled in two layers using two aluminum plate molds with a hole of 3.7 mm diameter. The surface of first layer of cured composite was prepared by one of five methods as followings, thereafter second layer of composite was filled and cured: Group 1 - OIL is allowed to remain on the surface of cured composite; Group 2 - OIL was removed by rubbing with acetone-soaked cotton; Group 3 - formation of the OIL was inhibited using a Mylar strip; Group 4 - OIL was covered with glycerin and light-cured; Group 5 (control) - composite was bulk-filled in a layer. The interfacial shear bond strength between two layers was tested and the fracture modes were observed. To investigate the propagation of polymerization reaction from active area having a photo-initiator to inactive area without the initiator, a flowable composite (Aelite Flow) or an adhesive resin (Adhesive of ScotchBond Multipurpose) was placed over an experimental composite (Exp_Com) which does not include a photoinitiator and light-cured. After sectioning the specimen, the cured thickness of the Exp_Com was measured.

The bond strength of group 2, 3 and 4 did not show statistically significant difference with group 1. Groups 3 and 4 were not statistically significant different with control group 5. The cured thicknesses of Exp_Com under the flowable resin and adhesive resin were 20.95 (0.90) um and 42.13 (2.09), respectively.

Keywords: Oxygen inhibition layer, Interfacial bonding, Resin composite, Flowable composite, Adhesive resin, Cured thickness

Figures and Tables

Figure 1

Arrangements of two molds for testing the interfacial shear bond strength. A: aluminum mold, B: hole for composite (diameter = 3.7 mm), C: hole for mounting jig connecting to an universal testing machine.

Figure 2

Specimen preparations for measuring the thickness of the interfacial polymerization propagation.

Figure 3

Interfacial shear bond strength between two resin composite layers according to the interfacial treatments. Group 1: remained oxygen inhibition layer at the interface, Group 2: removed oxygen inhibition layer with acetone, Group 3: inhibited the formation of oxygen inhibition layer by Mylar strip, Group 4: OIL was covered with glycerin and light-cured, Group 5: control group of bulk-filled composite. Groups within same bar did not show statistically significant differences.

Figure 4

Distribution of the interfacial fracture modes according to the interfacial treatments (n = 20).

Figure 5

(a) Cured layer of Exp_Com by the propagation of the polymerization reaction induced from Aelite Flow, or (b) from Adhesive resin of ScotchBond Multipurpose, (c) cured layer thickness of Exp_Com according to the interfacing resins. (AF, Aelite Flow; AR, Adhesive resin of ScotchBond Multipurpose.)

References

1. Andrzejewska E, Lindén LÅ, Rabek JF. The role of oxygen in camphorquinone-initiated photopolymerization. Macromol Chem Phys. 1998. 199:441–449.

2. Gauthier MA, Stangel I, Ellis TH, Zhu XX. Oxygen inhibition in dental resins. J Dent Res. 2005. 84:725–729.

3. Truffier-Boutry D, Place E, Devaux J, Leloup G. Interfacial layer characterization in dental composite. J Oral Rehabil. 2003. 30:74–77.

4. Velazquez E, Vaidyanathan J, Vaidyanathan TK, Houpt M, Shey Z, von Hagen S. Effect of primer solvent and curing mode on dentin shear bond strength and interface morphology. Quintessence Int. 2003. 34:548–555.

5. Kupiec KA, Barkmeier WW. Laboratory evaluation of surface treatments of composite repair. Oper Dent. 1996. 21:59–62.

6. Suh BI. Oxygen-inhibited layer in adhesion dentistry. J Esthet Restor Dent. 2004. 16:316–323.

7. Dall'Oca S, Papacchini F, Goracci C, Cury AH, Suh BI, Tay FR, Polimeni A, Ferrari M. Effect of oxygen inhibition on composite repair strength over time. J Biomed Mater Res B Appl Biomater. 2007. 81:493–498.

8. Finger WJ, Lee KS, Podszun W. Monomers with low oxygen inhibition as enamel/dentin adhesives. Dent Mater. 1996. 12:256–261.

9. Rueggeberg FA, Margeson DH. The effect of oxygen inhibition on an unfilled/filled composite system. J Dent Res. 1990. 69:1652–1658.

10. Eliades GC, Caputo AA. The strength of layering technique in visible light-cured composites. J Prosthet Dent. 1989. 61:31–38.

11. Lewis G, Johnson W, Martin W, Canerdy A, Claburn C, Collier M. Shear bond strength of immediately repaired light-cured composite resin restorations. Oper Dent. 1998. 23:121–127.

12. Ruyter IE. Unpolymerized surface layers on sealants. Acta Odontol Scand. 1981. 39:27–32.

13. Harry RA, Frederick WL, James EM. Contemporary polymer chemistry. 2003. 3rd Ed. Pearson Education Inc..

14. Bala O, Olmez A, Kalayci S. Effect of LED and halogen light curing on polymerization of resin-based composites. J Oral Rehabil. 2005. 32:134–140.

TOOLS

Similar articles