Lee, Jung, Cho, and Min: Metallosis after Revision of a Fractured Ceramic Head onto a Metal-on-Polyethylene Articulation - A Case Report -

Abstract

A ceramic articulation thought to be superior to metal-on-polyethylene due to its extremely low coefficient of friction and its potential for resistance to wear. But ceramic is brittle, which makes it theoretically susceptible to fracture. Although many authors have reported that metal-on-polyethylene articular pairing had good results after a ceramic head fracture, there have been few reports about complication due to the remaining ceramic particles after revision surgery. We report here on a case of severe metallosis that was thought to be due to third body wear by the remaining fractured ceramic particles after revision total hip arthroplasty.

Figures and Tables

Fig. 1
Radiographs of both femurs taken 4 weeks after each surgery show a well-fixed cup and stem.
jkoa-43-501-g001
Fig. 2
A radiograph shows the fracture of the ceramic femoral head.
jkoa-43-501-g002
Fig. 3
(A) A radiograph immediately before the left hip re-revision surgery shows the bubble sign around the left hip that indicates severe metallosis. (B) A photograph during the re-revision THA reveals fragmented ceramic particles in the black tissue, indicating metallosis.
jkoa-43-501-g003
Fig. 4
(A) Many scratches were observed on the abraded surface of the metal head on SEM. (B) Many large particles were embedded in the worn surface of the polyethylene as documented by SEM. (C) Those particles contained aluminum and oxygen on EDS examination.
jkoa-43-501-g004
Fig. 5
A photograph shows an example of a metal adapter that, like an extension piece, is fitted onto the deformed cone.
jkoa-43-501-g005

References

1. Allain J, Roudot-Thoraval F, Delecrin J, Anract P, Migaud H, Goutallier D. Revision total hip arthroplasty performed after fracture of a ceramic femoral head. A multicenter survivorship study. J Bone Joint Surg Am. 2003. 85:825–830.
2. Archibeck MJ, Jacobs JJ, Black J. Alternate bearing surfaces in total joint arthroplasty: biologic considerations. Clin Orthop Relat Res. 2000. 379:12–21.
3. Boutin P. Total arthroplasty of the hip by fritted aluminum prosthesis. Experimental study and 1st clinical applications. Rev Chir Orthop Reparatrice Appar Mot. 1972. 58:229–246.
4. Callaway GH, Flynn W, Ranawat CS, Sculco TP. Fracture of the femoral head after ceramic-on-polyethylene total hip arthroplasty. J Arthroplasty. 1995. 10:855–859.
5. Kempf I, Semlitsch M. Massive wear of a steel ball head by ceramic fragments in the polyethylene acetabular cup after revision of a total hip prosthesis with fractured ceramic ball. Arch Orthop Trauma Surg. 1990. 109:284–287.
crossref
6. Matziolis G, Perka C, Disch A. Massive metallosis after revision of a fractured ceramic head onto a metal head. Arch Orthop Trauma Surg. 2003. 123:48–50.
crossref
7. Miki H, Sugano N, Yamamura M, Nakamura N, Nishii T, Yoshikawa H. Serious metallosis of a metal head due to fragmented ceramic screws in a cemented THA. Arch Orthop Trauma Surg. 2006. 126:192–196.
crossref
8. Otsuka NY, Schatzker J. A case of fracture of a ceramic head in total hip arthroplasty. Arch Orthop Trauma Surg. 1994. 113:81–82.
crossref
9. Pulliam IT, Trousdale RT. Fracture of a ceramic femoral head after a revision operation. A case report. J Bone Joint Surg Am. 1997. 79:118–121.
crossref
10. Torán MM, Cuenca J, Martinez AA, Herrera A, Thomas JV. Fracture of a ceramic femoral head after ceramic-on-ceramic total hip arthroplasty. J Arthroplasty. 2006. 21:1072–1073.
crossref
TOOLS
Similar articles