Lee, Ku, Rhyu, Chung, and Park: Effects of fibrin-binding oligopeptide on osteopromotion in rabbit calvarial defects

Abstract

Purpose

Fibronectin (FN) has been shown to stimulate bone regeneration in animal models. The aim of this study was to evaluate the capacity of bovine bone mineral coated with synthetic oligopeptides to enhance bone regeneration in rabbit calvarial defects.

Methods

Oligopeptides including fibrin-binding sequences of FN repeats were synthesized on the basis of primary and tertiary human plasma FN structures. Peptide coated and uncoated bone minerals were implanted into 10 mm calvarial defects in New Zealand white rabbits, and the animals were sacrificed at 4 or 8 weeks after surgery. After specimens were prepared, histologic examination and histomorphometric analysis were performed.

Results

At 4 weeks after surgery, the uncoated groups showed a limited amount of osteoid formation at the periphery of the defect and the oligopeptide coated groups showed more osteoid formation and new bone formation in the center of the defect as well as at the periphery. At 8 weeks, both sites showed increased new bone formation. However, the difference between the two sites had reduced.

Conclusions

Fibrin-binding synthetic oligopeptide derived from FN on deproteinized bovine bone enhanced new bone formation in rabbit calvarial defects at the early healing stage. This result suggests that these oligopeptides can be beneficial in reconstructing oral and maxillofacial deformities or in regenerating osseous bone defects.

INTRODUCTION

Various graft materials have been widely used in the reconstruction of maxillofacial deformities and alveolar bone defects. Ideal grafts should promote the repair by ingrowth of new reparative tissue and should allow the delivery of biological factors to stimulate bone regeneration. Such substitutes should also provide physical strength and protection of the underlying structures during healing and should prevent the ingrowth of soft tissue.
Although autogenous bone is regarded as the gold standard in osseous reconstruction procedures, donor site morbidity, complications, hospital stays, cost, unpredictable graft resorption, and limited volume availability have been considered disadvantages [1-4].
Allografts, xenografts, and synthetic materials have been shown to promote osseous defect filling in humans [5]. Xenografts consist of bone mineral from animals or bone-like minerals derived from corals or algae [6], and deproteinized bovine bone (DBB) has a long history of successful use in filling in bone defects and maxillary sinus floor grafting [7-12]. As proteins in bovine bone have been extracted to avoid immunologic rejection, DBB acts just as an osteoconductive scaffold. However, using an osteoconductive grafting material may prolong the healing period, which may cause clinical shortcomings. Therefore, reliable bone regeneration requires the additional application of suitable bioactive substances to the surface of the grafted material in order to enhance osteoblast differentiation and proliferation.
In order to accelerate new bone formation, there have been many attempts to combine DBB with proteins or cytokines such as recombinant human bone morphogenic protein-2 and growth factors [13,14]. However, usage of whole natural protein imposes many disadvantages, including instability from enzymatic degradation, difficulties in obtaining stable attachment, nonspecific binding to other types of cells, immunogenecity, reduced material availability, relatively high cost, and sterilization problems [15,16]. Therefore, synthetic oligopeptides, which contain the active binding sequences of the natural protein, are regarded to be attractive alternatives, due to their ease of synthesis, handling convenience, and the reduced immunogenicity.
Fibronectin (FN), a major component of extracellular matrix (ECM), mediates a wide variety of cellular interactions with the ECM and plays important roles in cell adhesion, migration, growth, and differentiation [17]. It is a heterodimeric glycoprotein and interacts with cells and transmits signals through many receptors. FN has a remarkably wide variety of functional activities besides binding to cell surfaces through integrins. It binds to a number of biologically important molecules that include heparin, collagen/gelatin, and fibrin, and these interactions are mediated by several distinct structural and functional domains.
The FN subunit contains two fibrin binding sites. Among these two sites, the major site close to the amino terminus serves as a transglutamination site for activated factor XIII, crosslinking FN to various other proteins including fibrin, fibrinogen, and other FN [18]. The N-terminal site binds first due to its higher rate/affinity of fibrin binding, followed by the C-terminal site, which may then strengthen the fibrinbinding interactions of FN. Interaction of FN with fibrin mediated by factor XIII transglutaminase is thought to be important for cell adhesion or cell migration into fibrin clots. After tissue injury, a blood clot formation serves the dual role of restoring vascular integrity and serving as a temporary scaffold for the wound healing process. Fibrin and plasma FN, the major protein component of blood clots, are vascular essentials to these functions [19]. In blood clotting systems, after fibrin deposition, plasma FN-fibrin matrix is covalently cross-linked, and then it promotes fibroblast adhesion, spreading, and migration into the clot [20,21]. Fibroblast migration leads to deposition of cellular FN, which serves as a temporary scaffold for further recruitment of cells and granulation tissue formation in the wound healing process [22]. Therefore, cross-linked FN is an absolute requirement for the wound healing process. FN can also be cross-linked to collagen, a reaction that is potentially important for collagen fibrillogenesis [23].
In this study, we used DBB coated with synthetic oligopeptides including fibrin binding sites from amino-terminal FN fragments to evaluate the osteopromotive effect of this peptide in rabbit calvarial defects.

MATERIALS AND METHODS

Preparation of peptide-coated deproteinized bovine bone

Oligopeptides including fibrin-binding sequences of FN repeats were designed on the basis of primary and tertiary human plasma FN structures (FINC-HUMAN: P02751 [24]). A solid-phase peptide synthesizing system was used to prepare these oligopeptides. The amino acid sequence was as follows: CTSRNRCNDQ.
Deproteinized cancellous bovine bone particles (OCS-B, NIBEC, Seoul, Korea) ranging from 0.2 to 1.0 mm were soaked in 3.1 mM synthetic peptide in distilled water. They were kept for 18 hours at room temperature after gentle shaking to ensure equilibration of the peptide with all exposed surfaces of the microporous bone. After freeze drying, the bone particles were sterilized by γ-radiation.

Surgical procedures

Twelve New Zealand white male rabbits weighing 2.1 to 2.5 kg were used. Two circular defects were made in the parietal bone of each rabbit. The surgical procedures for this investigation were performed according to recognized techniques approved by the Institute of Laboratory Animal Resources, Seoul National University. Each animal was premedicated according to their weight with an intramuscular injection of tiletamine/zolazepam (0.2 mg/kg body weight) and xylazine (5 mg/kg body weight). After the surgical site was disinfected with betadine, local anesthesia was provided using a 2% lidocaine solution. An incision was made along the midline of the scalp from a point midway between the bases of the ears to approximately 5 cm anteriorly through the full thickness of the skin. Sharp subperiosteal dissection reflected the pericranium from the outer table of the cranial vault exposing the parietal bones. An electric drill with an 8 mm inner diameter trephine bur was used to create bilateral full thickness calvarial defects. The defect sizes that resulted ranged from 9.5 to 10 mm. The peptide coated bone mineral was implanted on one side, and uncoated bone mineral was implanted on the other side served as a control (Fig. 1). Care was taken to prevent displacement of the bone particles into the other defect to prevent a spill-over effect. The pericranium and skin were closed with 5-0 chromic gut and 4-0 silk sutures, respectively. Six of the animals were euthanized at 4 weeks, and the others at 8 weeks. No specimen showed any evidence of infection or foreign body reaction, and all wounds healed unevenfully.

Histologic analysis

Each animal was euthanized at 4 or 8 weeks. The cranial vault was carefully removed from each animal and embedded in the media (Technovit 7200, Exakt, Hamburg, Germany) after 10% neutral buffered formalin treatment with a series of ethanol solutions of increasing concentrations. The embedded specimens were mounted on acrylic glass slabs and sections were cut from the middle of each specimen. The sections were grounded and polished to a final thickness of 40 µm. The thin sections were stained with hematoxylin-eosin for quantification of the amount of bone regeneration under light microscopy.

Histomorphometric analysis

Computer-assisted histomorphometric analysis was done after conventional microscopic examination. Measurements of newly formed bone and graft particles were obtained using a software package (TDI Scope Eye, Techsan, Seoul, Korea) coupled with a digital camera on a light microscope (BH-2, Olympus Optical, Osaka, Japan). The proportion of new bone and DBB particles over the entire surface was measured. The total perimeter of DBB particles and the portion of the perimeter of DBB particles in contact with bone tissue were also measured, and the degree (%) of new bone-DBB contact was calculated. Two sections were obtained from each biopsy and visual fields from each biopsy were measured.

Statistical analysis

Data were reported as mean ± SD with a significance level of P < 0.05. A Mann-Whitney U test was used to compare data from histomorphometric analyses.

RESULTS

Histologic evaluation

At 4 weeks after surgery, in the sites with uncoated bone, the defect area was primary occupied by the graft material and the connective tissue (Fig. 2A). Few immature osteoid formations were observed in the central part of the defect and newly formed bone was near the defect border (Figs. 3A and 4A). On the other hand, the new bone formation in the site with peptide coated bone was more enhanced than that of the control sites (Fig. 2B). Most of the specimens showed new bone formation extending to the central part of the defect (Fig. 3B). Evidence of osteoid formation adjacent to the graft material was found and coalescence of the new bone with graft material was observed (Fig. 4B).
At 8 weeks, the amount of the new bone was greater than that observed at 4 weeks in both groups. New bone was deposited evenly around the graft material and extended to the central area of the defects (Fig. 5). The bone mineral was integrated with the new bone and newly formed bones had connected to each other (Fig. 6), especially in the peptide coated groups. In higher magnification, multiple bony islands filled the central part of the defect (Fig. 7A) and connected each other. In the peptide coated group, new bone showed a more mature pattern (Fig. 7B). The particles of DBB were easily identified. Neither resorption lacunae nor active osteoclasts were found in specimens at 4 and 8 weeks.

Histomorphometric evaluation

The average areas occupied by grafted materials are shown in Table 1. There was no significant difference between the groups at 4 and 8 weeks (P > 0.05). The average areas occupied by new bone was 15.29 ± 1.93% for the control group and 18.84 ± 1.75% for the experimental group at 4 weeks. At 8 weeks, the average areas were 18.14 ± 2.81% and 19.00 ± 2.08%, respectively (Table 2, Fig. 8). There was a significant difference in the regeneration areas between the control and experimental group at 4 weeks (P < 0.05). At 8 weeks, no statistical difference was observed (P > 0.05).
The average bone-DBB contact ratios were 14.50 ± 3.53% for the control group and 19.33 ± 3.37% for the experimental group at 4 weeks. At 8 weeks, the average contact ratios were 17.36 ± 3.54% and 19.03 ± 2.79%, respectively (Table 3, Fig. 9). While there was a significant difference in the contact ratios between control and experimental groups at 4 weeks (P < 0.05), but no statistical difference in 8 weeks (P > 0.05).

DISCUSSION

In this study, fibrin-binding synthetic oligopeptide derived from FN was used to coat the DBB, and the effect was evaluated. Histologic observation showed that no adverse response was induced by graft bone, with or without peptide. At 4 weeks after surgery, the uncoated bone groups showed evidence of osteoid formation near the defect periphery area; however, at the center area, osteoid formation was not observed. On the other hand, in the coated bone groups, new bone formation was observed in the defect center as well as the defect periphery. Among the 4-week models, new bone formation was more evident in the coated bone group than in the uncoated group. After 8 weeks, new bone formation was observed throughout the defect area in both cases. Newly formed bones around the DBB were connected to each other and showed a more advanced stage of remodeling and maturation. In the histomorphometric analysis, the percentage gain of bone regeneration was calculated as the ratio of the area of newly formed bone to that of the original defects. A significant finding in this study is the accelerated formation of new bone observed within the experimental groups at 4 weeks. In the 4-week model, new bond formation in the coated group was 18.84 ± 1.75% compared with 15.29 ± 1.93% in the uncoated group, and there was a statistical difference between the two cases (P < 0.05). By 8 weeks, the difference had decreased and a statistically significant difference was not observed. The new bone ratio in the control group was 18.14 ± 2.81% and in the experimental group was 19.00 ± 2.08%. The ratio of the contact surface showed a similar pattern. In the 4-week models, the contact surface ratio was 14.50 ± 3.53% and 19.33 ± 3.37%, and in the 8-week models the ratio was 17.36 ± 3.54% and 19.03 ± 2.79%, for the control and experimental groups, respectively. There was no statistically significant difference in the 8-week models (P > 0.05). Okazaki et al. [25] found that DBB grafted in rabbit calvarial defects showed gradual increases in the proportion of newly formed bone at 4 and 8 weeks and the proportion of newly formed bone-graft particle contact length showed significant increases at 4 weeks and no significant changes at 8 weeks, which are consistent with our finding that fibrin-binding synthetic oligopeptide derived from FN coated on demineralized bovine bone enhanced new bone formation in rabbit calvarial defects, especially in the early healing stage.
FN is a major glycoprotein in the ECM, which binds to integrins and regulates cell survival, growth, motility, and differentiation. Many attempts have been made to promote bone regeneration using FN; however, the results have been controversial. In 2001, Camargo et al. [26] evaluated the ability of FN to augment the regenerative effects of a bovine-derived bone in human periodontal defects. They found that a significant difference between the regenerative treatment modalities could not be demonstrated. On the other hand, Lekovic et al. [27] used bovine porous bone mineral in combination with an autologous fibrinogen/FN system in the treatment of intrabony periodontal defects in humans. They found that the autologous fibrin/fibrinogen system used in combination with bovine porous bone mineral has some effect in promoting probing depth reduction, clinical attachment gain, and defect fill when employed as regenerative therapy for intraosseous lesions in humans. Di Bella et al. [28] reported that surface treatment with FN promotes bone formation within the polylactic acid scaffold in a critical-sized defect rabbit model with or without autologous adipose-derived mesenchymal stem cells in combination. In 2008, Schonmeyr et al. [29] found in vitro attachment and proliferation of bone-forming cells on hydroxyapatite is significantly increased by pretreatment with FN/fetal calf serum, but this difference is less profound and not significant in vivo. This controversy could be due to the common shortcomings of whole protein usage, including instability to enzymatic degradation, unexpected effects of other domains, nonspecific binding to other types of cells, difficulty in obtaining stable attachment, and even integrin blocking effects [15,16]. Therefore, small synthetic peptides with active binding sequences of natural proteins have been proposed as alternatives. In our previous study, fibrin- binding synthetic oligopeptide showed marked enhancement in periodontal ligament cell proliferation, attachment, and mineralization [30]. These results can be compared with those obtained from previous studies conducted by other researchers using similar animal models. Augmentation of the maxillary sinus using DBB with or without recombinant human bone morphogenic protein (rhBMP)-7 was performed by Terhyeden et al. [31] using DBB in minipigs. A significant increase in bone formation was found (38.6-80.0%) when rh-BMP-7 was added to the graft. In 2007, Park et al. [32] demonstrated that the use of DBB with a synthetic rhBMP-7 seems to be a more beneficial material for bone regeneration in the early healing period. They detected a significant difference in the percentage of new bone formation between peptide-coated group and peptide-uncoated group: 6.60 ± 0.89% and 23.72 ± 1.73% at 2 weeks, 34.77 ± 3.31% and 42.27 ± 2.35% at 4 weeks, respectively. On the contrary, Gordjestani et al. [33] investigated the influence of osteopontin on bone repair in rabbit calvarial defects. There were no statistically significant differences in total bone formation between defects filled with osteopontin-hydroxyapatite and those with hydroxyapatite only. The differences identified in the amount of reparative tissue seen in our study and previous other studies can be explained by the biomaterials used for each study. Compared with other studies, our study observed a lower percentage of new bone gain, but fibrin-binding synthetic oligopeptide derived from FN might have some effect as a DBB coating material, especially in the early bone healing stage.
The creation of nonunions in animals within the calvaria and mandible was size dependent. A critical size defect (CSD) was defined as the smallest size intraosseous wound in a particular bone and species of animal that will not heal spontaneously during the lifetime of the animal [34]. It was known that the size of a CSD was dependent on the breed and age of the experimental animal model used as well as the location of the defect. Frame [35] described the healing of 15-mm diameter defects in the calvaria of rabbits. After 24 and 36 weeks, the 15 mm diameter defects had healed by the formation of fibrous connective tissue. Also, Hollinger and Kleinschmidt [36] confirmed that untreated 15-mm cranial defects created in New Zealand white rabbits showed less than 10% bone regeneration after 48 weeks. However, Ascherman et al. [37] used 10-mm diameter defects as a CSD in their study of the 6-month histology of a quick-setting hydroxyapatite cement, with and without absorbable plates. In 2007, Pripatnanont et al. [38] used a bicortical 10 × 10 mm skull defect model in their study examining the osteoconductive ability of 3 bovine hydroxyapatites. After 8 weeks, the controls showed bone formation around the marginal bone, showing projection in a centripetal direction. In the upper and lower parts of the defect, woven bone was projected from the edges of the defects, whereas in the central part, only fibrous connective tissue occupied the defect.
Resorption and complete remodeling into new bone are the ideal outcomes of a grafting material. In this study, the ratio of grafted DBB did not change much according to the type of grafted material or healing period. The resorption of DBB has been a controversial subject in many studies. McAllister et al. [39] detected a decrease in the percentage of DBB, from 19 ± 14% to 6 ± 3% over a time period of 7.5-18 months in a chimpanzee study. Klinge et al. [40] found that DBB particles in defects of rabbit calvarial skulls had almost completely disappeared after 14 weeks of healing, as the effect of multinucleated cells. Based on these results, they suggested that DBB had been resorbed and replaced by vital bone. On the other hand, Schlegel [41] could identify DBB particles after a healing period of up to 7 years and Skoglund et al. [42] also suggested that DBB particles were slowly degraded and remained 44 months after augmentation of a maxillary alveolar ridge. Yildrim et al. [43] suggested that such a difference in bony healing of DBB is mainly influenced by the healing response of the individual patient and is less dependent on the healing time of the augmentation material. From a biologic point of view, resorption requires adhesion molecules (arginine-glycine-aspartic acid [RGD] sequence) for the attachment of osteoclastic cells to plasma and ECM, including FN, fibrinogen, vitronectin, type I collagen, osteopontin, and bone sialoprotein [44]. As DBB is free of proteins, osteoclastic resorption can probably not occur. However, Schwartz et al. [12] observed transforming growth factor-β and BMP-2 in DBB particles, which might explain the lacunae found in some DBB particles. Rooney et al. [45] interpreted possible signs of resorption as evidence of osteoclastic resorption mediated by later surface adsorption of proteins containing RGD sequences, such as FN or fibrinogen. In this study, we used fibrin binding sequences of FN as DBB coating material; therefore, the RGD sequence of FN is not included and results of the initial healing stage, that is, post-surgery 2 weeks, were not included. Further investigation about DBB resorption is needed.
In this study, the peptide mentioned above was used to coat DBB, and the effects on bone regeneration were evaluated. The study was done at 4-week and 8-week periods to evaluate bone formation in the early and late healing period. Histologic observation showed that no adverse response was induced by the graft, with or without peptide. The amount of new bone at sites with peptide-coated bone mineral was greater than at sites with uncoated bone. The new bone was deposited evenly around the graft material, and the bone mineral was integrated fully with the new bone in experimental sites. By histomorphometric analysis, the percentage gain in bone regeneration was calculated as the ratio of the area of newly formed bone to the area of the original defect. A significant finding in this study is the accelerated formation of new bone observed at experimental sites compared to control sites at the early healing stage. However, more studies are required to determine the quantity of peptide suitable for optimal bone regeneration and DBB coating method.
These results suggest that the formation of new bone and the normal healing process occur more rapidly when synthetic oligopeptide is used.

Figures and Tables

Figure 1
Bilateral calvarial defects were created in parietal bones.
jpis-40-211-g001
Figure 2
(A) Histologic view of uncoated bone group after 4 weeks. Newly formed bone was found at the periphery of the defect; however, there was little, if any, new bone formation in the central part of the defect. Arrows indicate the margin of the bone defect. (B) Histologic view of the peptide coated bone group after 4 weeks. New bone formation was obvious and observed in the central part of the defect. Arrows indicate the margin of the bone defect (H&E staining).
jpis-40-211-g002
Figure 3
(A) Histologic view of the uncoated bone group at 4 weeks. Higher magnification of the area marked in Fig. 2A. A very limited amount of bone formation around the graft material is noted. (B) Histologic view of the coated bone group at 4 weeks. Higher magnification of the area marked in Fig. 2B. New bone formation was observed in the central area of the defect (H&E staining).
jpis-40-211-g003
Figure 4
(A) Higher magnification of Fig. 3A. A very limited amount of immature osteoid formation around the graft material was noted. (B) Higher magnification of the area marked in Fig 3B. Osteoid formation was noted around the graft material (▸). The newly generated bone seems well integrated with the graft material (⋆) (H&E staining).
jpis-40-211-g004
Figure 5
(A) Histologic view of the uncoated bone group after 8 weeks. New bone formation was noted throughout the defect. Arrows indicate the margin of the bone defect. (B) Histologic view of the peptide coated bone group after 8 weeks. New bone formation was obvious, and the defect tended to coalesce with new bone. Arrows indicate the margin of the bone defect (H&E staining).
jpis-40-211-g005
Figure 6
(A) Histologic view of the uncoated bone group at 8 weeks. Higher magnification of the area marked in Fig. 5A. New bone formation was observed in the central area of the defect. (B) Histologic view of the coated bone group at 8 weeks. Higher magnification of the area marked in Fig. 5B. New bone formation was observed evenly throughout the defect with highly cellular marrow spaces, osteoids, and osteoblsts (H&E staining).
jpis-40-211-g006
Figure 7
(A) Higher magnification of Fig. 6A. Multiple bony islands fill the central part of the defect (⇒). (B) Higher magnification of Fig. 6B. The grafted bone is integrated fully with the new bone (◂) and shows a more advanced stage of remodeling and consolidation (▸) (H&E staining).
jpis-40-211-g007
Figure 8
Percentages of newly formed bone after implantation for different periods using histomorphometric analysis. *There was a significant difference between the peptide coated bone group and uncoated bone group at 4 weeks (P < 0.05). **There was a significant difference between the 4-week and 8-week uncoated bone group (P < 0.05).
jpis-40-211-g008
Figure 9
Percentages of newly formed bone-deproteinized bovine bone contact after implantation for different periods using histomorphometric analysis. *There was a significant difference between the peptide coated bone group and uncoated bone group after 4 weeks (P < 0.05).
jpis-40-211-g009
Table 1
The ratio of the area of the grafted particles to the original defect (mean ± SD).
jpis-40-211-i001

There was no significant difference between the groups (P > 0.05).

Table 2
The ratio of the area of newly formed bone to the original defect (mean ± SD).
jpis-40-211-i002

a)There was a significant difference between the peptide coated bone group and uncoated bone group after 4 weeks (P < 0.05).

b)There was a significant difference between the 4-week and 8-week peptide-coated mineral groups (P < 0.05).

Table 3
The degree of bone-DBB contact (mean ± SD).
jpis-40-211-i003

DBB: deproteinized bovine bone.

a)There was a significant difference between the peptide coated bone group and uncoated bone group after 4 weeks (P < 0.05).

Notes

No potential conflict of interest relevant to this article was reported.

References

1. Hallman M, Cederlund A, Lindskog S, Lundgren S, Sennerby L. A clinical histologic study of bovine hydroxyapatite in combination with autogenous bone and fibrin glue for maxillary sinus floor augmentation. Results after 6 to 8 months of healing. Clin Oral Implants Res. 2001. 12:135–143.
crossref
2. Carlson ER, Marx RE. Part II. Mandibular reconstruction using cancellous cellular bone grafts. J Oral Maxillofac Surg. 1996. 54:889–897.
3. Petrovic L, Schlegel AK, Schultze-Mosgau S, Wiltfang J. Different substitute biomaterials as potential scaffolds in tissue engineering. Int J Oral Maxillofac Implants. 2006. 21:225–231.
4. Springer IN, Terheyden H, Geiss S, Harle F, Hedderich J, Acil Y. Particulated bone grafts: effectiveness of bone cell supply. Clin Oral Implants Res. 2004. 15:205–212.
5. Garrett S. Periodontal regeneration around natural teeth. Ann Periodontol. 1996. 1:621–666.
crossref
6. Jensen SS, Aaboe M, Pinholt EM, Hjorting-Hansen E, Melsen F, Ruyter IE. Tissue reaction and material characteristics of four bone substitutes. Int J Oral Maxillofac Implants. 1996. 11:55–66.
7. Fukuta K, Har-Shai Y, Collares MV, Lichten JB, Jackson IT. Comparison of inorganic bovine bone mineral particles with porous hydroxyapatite granules and cranial bone dust in the reconstruction of full-thickness skull defect. J Craniofac Surg. 1992. 3:25–29.
crossref
8. Haas R, Donath K, Fodinger M, Watzek G. Bovine hydroxyapatite for maxillary sinus grafting: comparative histomorphometric findings in sheep. Clin Oral Implants Res. 1998. 9:107–116.
crossref
9. Kasabah S, Simunek A, Krug J, Lecaro MC. Maxillary sinus augmentation with deproteinized bovine bone (Bio-Oss) and Impladent dental implant system. Part II. Evaluation of deprotienized bovine bone (Bio-Oss) and implant surface. Acta Medica (Hradec Kralove). 2002. 45:167–171.
crossref
10. Maiorana C, Redemagni M, Rabagliati M, Salina S. Treatment of maxillary ridge resorption by sinus augmentation with iliac cancellous bone, anorganic bovine bone, and endosseous implants: a clinical and histologic report. Int J Oral Maxillofac Implants. 2000. 15:873–878.
11. Merkx MA, Maltha JC, Freihofer HP. Incorporation of composite bone implants in the facial skeleton. Clin Oral Implants Res. 2000. 11:422–429.
crossref
12. Schwartz Z, Weesner T, van Dijk S, Cochran DL, Mellonig JT, Lohmann CH, et al. Ability of deproteinized cancellous bovine bone to induce new bone formation. J Periodontol. 2000. 71:1258–1269.
crossref
13. Barboza EP, Duarte ME, Geolas L, Sorensen RG, Riedel GE, Wikesjo UM. Ridge augmentation following implantation of recombinant human bone morphogenetic protein-2 in the dog. J Periodontol. 2000. 71:488–496.
crossref
14. Rocchietta I, Dellavia C, Nevins M, Simion M. Bone regenerated via rhPDGF-bB and a deproteinized bovine bone matrix: backscattered electron microscopic element analysis. Int J Periodontics Restorative Dent. 2007. 27:539–545.
15. Grzesik WJ, Ivanov B, Robey FA, Southerland J, Yamauchi M. Synthetic integrin-binding peptides promote adhesion and proliferation of human periodontal ligament cells in vitro. J Dent Res. 1998. 77:1606–1612.
crossref
16. Kantlehner M, Schaffner P, Finsinger D, Meyer J, Jonczyk A, Diefenbach B, et al. Surface coating with cyclic RGD peptides stimulates osteoblast adhesion and proliferation as well as bone formation. Chembiochem. 2000. 1:107–114.
crossref
17. Mosher DF. Fibronectin. 1989. San Diego: Academic Press.
18. Magnusson MK, Mosher DF. Fibronectin: structure, assembly, and cardiovascular implications. Arterioscler Thromb Vasc Biol. 1998. 18:1363–1370.
19. Corbett SA, Lee L, Wilson CL, Schwarzbauer JE. Covalent cross-linking of fibronectin to fibrin is required for maximal cell adhesion to a fibronectin-fibrin matrix. J Biol Chem. 1997. 272:24999–25005.
crossref
20. Grinnell F, Feld M, Minter D. Fibroblast adhesion to fibrinogen and fibrin substrata: requirement for cold-insoluble globulin (plasma fibronectin). Cell. 1980. 19:517–525.
crossref
21. Corbett SA, Wilson CL, Schwarzbauer JE. Changes in cell spreading and cytoskeletal organization are induced by adhesion to a fibronectin-fibrin matrix. Blood. 1996. 88:158–166.
crossref
22. Greiling D, Clark RA. Fibronectin provides a conduit for fibroblast transmigration from collagenous stroma into fibrin clot provisional matrix. J Cell Sci. 1997. 110:861–870.
crossref
23. Mosher DF, Schad PE, Kleinman HK. Inhibition of blood coagulation factor XIIIa-mediated cross-linking between fibronectin and collagen by polyamines. J Supramol Struct. 1979. 11:227–235.
crossref
24. Damsky CH. Extracellular matrix-integrin interactions in osteoblast function and tissue remodeling. Bone. 1999. 25:95–96.
crossref
25. Okazaki K, Shimizu Y, Xu H, Ooya K. Blood-filled spaces with and without deproteinized bone grafts in guided bone regeneration. A histomorphometric study of the rabbit skull using non-resorbable membrane. Clin Oral Implants Res. 2005. 16:236–243.
crossref
26. Camargo PM, Wolinsky LE, Ducar JP, Lagos R, Pirih FQ, Jeffcoat M, et al. The effect of fibronectin and a bone xenograft on regenerative treatment: a feasibility study. Compend Contin Educ Dent. 2006. 27:560–568.
27. Lekovic V, Camargo PM, Weinlaender M, Vasilic N, Djordjevic M, Kenney EB. The use of bovine porous bone mineral in combination with enamel matrix proteins or with an autologous fibrinogen/fibronectin system in the treatment of intrabony periodontal defects in humans. J Periodontol. 2001. 72:1157–1163.
crossref
28. Di Bella C, Farlie P, Penington AJ. Bone regeneration in a rabbit critical-sized skull defect using autologous adipose-derived cells. Tissue Eng Part A. 2008. 14:483–490.
crossref
29. Schonmeyr BH, Wong AK, Li S, Gewalli F, Cordiero PG, Mehrara BJ. Treatment of hydroxyapatite scaffolds with fibronectin and fetal calf serum increases osteoblast adhesion and proliferation in vitro. Plast Reconstr Surg. 2008. 121:751–762.
crossref
30. Lee JA, Ku Y, Park YJ, Koo KT, Kim TI, Seol YJ, et al. The biologic effect of fibrin-binding synthetic oligopeptide on periodontal ligament cells. J Korean Acad Periodontol. 2009. 39:45–52.
crossref
31. Terheyden H, Jepsen S, Moller B, Tucker MM, Rueger DC. Sinus floor augmentation with simultaneous placement of dental implants using a combination of deproteinized bone xenografts and recombinant human osteogenic protein-1. A histometric study in miniature pigs. Clin Oral Implants Res. 1999. 10:510–521.
crossref
32. Park JB, Lee JY, Park HN, Seol YJ, Park YJ, Rhee SH, et al. Osteopromotion with synthetic oligopeptide-coated bovine bone mineral in vivo. J Periodontol. 2007. 78:157–163.
crossref
33. Gordjestani M, Dermaut L, De Ridder L, De Waele P, De Leersnijder W, Bosman F. Osteopontin and bone metabolism in healing cranial defects in rabbits. Int J Oral Maxillofac Surg. 2006. 35:1127–1132.
crossref
34. Schmitz JP, Hollinger JO. The critical size defect as an experimental model for craniomandibulofacial nonunions. Clin Orthop Relat Res. 1986. 205:299–308.
crossref
35. Frame JW. A convenient animal model for testing bone substitute materials. J Oral Surg. 1980. 38:176–180.
36. Hollinger JO, Kleinschmidt JC. The critical size defect as an experimental model to test bone repair materials. J Craniofac Surg. 1990. 1:60–68.
crossref
37. Ascherman JA, Foo R, Nanda D, Parisien M. Reconstruction of cranial bone defects using a quick-setting hydroxyapatite cement and absorbable plates. J Craniofac Surg. 2008. 19:1131–1135.
crossref
38. Pripatnanont P, Nuntanaranont T, Vongvatcharanon S, Limlertmongkol S. Osteoconductive effects of 3 heat-treated hydroxyapatites in rabbit calvarial defects. J Oral Maxillofac Surg. 2007. 65:2418–2424.
crossref
39. McAllister BS, Margolin MD, Cogan AG, Buck D, Hollinger JO, Lynch SE. Eighteen-month radiographic and histologic evaluation of sinus grafting with anorganic bovine bone in the chimpanzee. Int J Oral Maxillofac Implants. 1999. 14:361–368.
40. Klinge B, Alberius P, Isaksson S, Jonsson J. Osseous response to implanted natural bone mineral and synthetic hydroxylapatite ceramic in the repair of experimental skull bone defects. J Oral Maxillofac Surg. 1992. 50:241–249.
crossref
41. Schlegel AK. Bio-Oss bone replacement material. Long-term results with Bio-Oss bone replacement material. Schweiz Monatsschr Zahnmed. 1996. 106:141–149.
42. Skoglund A, Hising P, Young C. A clinical and histologic examination in humans of the osseous response to implanted natural bone mineral. Int J Oral Maxillofac Implants. 1997. 12:194–199.
43. Yildirim M, Spiekermann H, Handt S, Edelhoff D. Maxillary sinus augmentation with the xenograft Bio-Oss and autogenous intraoral bone for qualitative improvement of the implant site: a histologic and histomorphometric clinical study in humans. Int J Oral Maxillofac Implants. 2001. 16:23–33.
44. Pierschbacher MD, Ruoslahti E. Variants of the cell recognition site of fibronectin that retain attachment-promoting activity. Proc Natl Acad Sci U S A. 1984. 81:5985–5988.
crossref
45. Rooney MM, Farrell DH, van Hemel BM, de Groot PG, Lord ST. The contribution of the three hypothesized integrin-binding sites in fibrinogen to platelet-mediated clot retraction. Blood. 1998. 92:2374–2381.
crossref
TOOLS
ORCID iDs

Young Ku
https://orcid.org/http://orcid.org/0000-0001-5682-0604

Similar articles